Thermoplastic resin composition

ABSTRACT

The thermoplastic resin composition of the present invention contains 
     (a) a resin composition consisting of 
     (1) at least one polypropylene resin (E) selected from the group consisting of 
     (i) a graft polypropylene (A) obtained by graft polymerizing an unsaturated carboxylic acid or a derivative thereof onto a polypropylene (C), 
     (ii) a graft polypropylene (B) obtained by graft polymerizing an unsaturated carboxylic acid or a derivative thereof and an unsaturated aromatic monomer onto a polypropylene (C), 
     (iii) a composition (D) selected from the group consisting of 
     a composition of a polypropylene (C) and the graft polypropylene (A), 
     a composition of a polypropylene (C) and the graft polypropylene (B), 
     a composition of a polypropylene (C), the graft polypropylene (A) and 
     the graft polypropylene (B), and 
     (2) a saturated polyester resin (F) 
     (b) an epoxy group-containing copolymer (G), and 
     (c) at least one member selected from the group consisting of 
     (i) a rubbery substance (H), 
     (ii) a modified rubbery substance (I), and 
     (iii) a mixture of the rubbery substance (H) and the modified rubbery substance (I), the content of the saturated polyester resin (F) in the thermoplastic resin composition being not more than 50% by weight; or 
     (a) either a graft resin composition (J) obtained by graft polymerizing an unsaturated carboxylic acid or a derivative thereof onto a mixture of a polypropylene (C) and a rubbery substance (H), or a graft resin composition (K) obtained by graft polymerizing an unsaturated carboxylic acid or a derivative thereof and an unsaturated aromatic monomer onto a mixture of a polypropylene (C) and a rubbery substance (H), 
     (b) a saturated polyester resin (F), 
     (c) an epoxy group-containing copolymer (G), and 
     (d) a polypropylene (C); 
     which thermoplastic resin composition is suitably used in the fields where high level of heat resistance, impact resistance, and especially low-temperature impact resistance are required.

This application is a continuation of application Ser. No. 07/661,241,filed Feb. 27, 1991, now abandoned.

The present invention relates to a novel thermoplastic polypropyleneresin composition which is utilizable in a form of molded articles,sheets, films, etc., by means of injection molding, extrusion molding.

More specifically, the present invention relates to a novelthermoplastic polypropylene-based resin composition which has anexcellent physical property balance and excellent appearance, and whichis formed by incorporating an epoxy group-containing copolymer into apolypropylene-based resin and an unsaturated polyester resin.

Polypropylenes have heretofore been widely used in the form of moldedarticles, films and sheets due to their excellent moldingprocessability, toughness, water resistance, gasoline resistance,chemical resistance, etc., and due to their low specific gravity and lowcost.

However, polypropylenes have defect, which should be improved, in heatresistance, stiffness, impact resistance, scratch resistance, coatingproperties, adhesive properties, printability, etc., and these defectsconstitute an obstacle to the application of polypropylenes to new areasin practical use.

In order to improve coating properties, adhesive properties,printability, etc., of the above properties, JP-B-58-47418 andJP-A-58-49738, etc., propose a method of partially or whollygraft-modifying a polypropylene with an unsaturated carboxylic acid oran anhdyride thereof such as maleic anhydride, for example. However,even when such a modified polypropylene is used, the impact resistance,heat resistance, stiffness and the other properties are not essentiallyimproved.

Meanwhile, unsaturated polyester resins are widely used as anengineering resin having characteristic heat resistance, stiffness,strength and oil resistance in the fields of automobile parts andelectric and electronic parts. However, it is desired to improve theunsaturated polyester resins further in moldability, impact resistance,water resistance and chemical resistance. The unsaturated polyesterresins further have inherent disadvantages in that they have a highspecific gravity and are expensive.

From such a viewpoint, a wide new area in use is expected if athermoplastic resin having features of both a polypropylene-based resinand a saturated polyester resin can be obtained by blending apolypropylene-based resin selected from a graft polypropylene and agraft polypropylene/polypropylene composition with an saturatedpolyester resin.

However, it has been conventionally considered that apolypropylene-based resin is poor in compatibility and dispersibilitywith a saturated polyester resin, and a mere blend of these actuallycauses the following problems.

(1) A molten polymer shows a high Barus effect, and it is substantiallyimpossible to take off an extruded strand stably. Thus, the mere blendof these resin lowers the molding workability of the resulting blend toa great extent.

(2) The injection-molded article of the resulting blend shows an extremenonuniformity and poor appearance due to the occurrence of flow marks sothat it is not practically usable as automobile-parts, electric orelectronic parts, etc.

(3) The molded article formed of a mixture of a polypropylene-basedresin with a saturated polyester resin often show lower values inmechanical properties, in particular, impact resistance, tensileelongation, etc., than expected from the additivity of the individualproperties of these components.

According to the method described in JP-A-61-60746, it is possible toimpart a polypropylene and a saturated polyester, which are inherentlyincompatible with each other, with mutual compatibility anddispersiblity by incorporating an epoxy group-containing copolymer intoa mixture of a polypropylene-based resin selected from a modifiedpolypropylene and a modified polypropylene/polypropylene composition anda saturated polyester resin, and it is thus possible to produce athermoplastic resin composition which has well balanced physicalproperties among molding processability, stiffness, heat resistance,impact resistance, scratch resistance, coating properties, oilresistance, chemical resistance, water resistance, etc., and theexcellent appearance uniformity and smoothness.

However, the thermoplastic resin composition for use as automobile partsand electric and electronic parts is required to have a high-level ofheat resistance, impact resistance, etc., and in particular, alow-temperature impact resistance. As a result of a diligent study inorder to further improve the heat resistance and impact resistance ofthe thermoplastic resin composition disclosed in JP-A-61-60746, thepresent invention has been completed.

According to the present invention, there are provided a thermoplasticresin composition which comprises:

(a) 100 parts by weight of a resin composition consisting of

(1) 1-99% by weight of at least one polypropylene resin (E) selectedfrom the group consisting of

(i) a graft polypropylene (A) obtained by graft polymerizing anunsaturated carboxylic acid or a derivative thereof onto a polypropylene(C),

(ii) a graft polypropylene (B) obtained by graft polymerizing anunsaturated carboxylic acid or a derivative thereof and an unsaturatedaromatic monomer onto a polypropylene (C),

(iii) a composition (D) selected from the group consisting of

a composition of a polypropylene (C) and a graft polypropylene (A)obtained by graft polymerizing an unsaturated carboxylic acid or aderivative thereof onto a polypropylene (C),

a composition of a polypropylene (C) and a graft polypropylene (B)obtained by graft polymerizing an unsaturated carboxylic acid or aderivative thereof and an unsaturated aromatic monomer onto apolypropylene (C),

a composition of a polypropylene (C), a graft polypropylene (A) obtainedby graft polymerizing an unsaturated carboxylic acid or a derivativethereof onto a polypropylene (C) and

a graft polypropylene (B) obtained by graft polymerizing an unsaturatedcarboxylic acid or a derivative thereof and an unsaturated aromaticmonomer onto a polypropylene (C), and

(2) 99-1% by weight of a saturated polyester resin (F),

(b) 0.1-300 parts by weight of an epoxy group-containing copolymer (G),and

(c) 0.1-300 parts by weight of at least one member selected from thegroup consisting of

(i) a rubbery substance (H),

(ii) a modified rubbery substance (I), and

(iii) a mixture of the rubbery substance (H) and the modified rubberysubstance (I),

the content of the saturated polyester resin (F) in the thermoplasticresin composition being not more than 50% by weight;

a thermoplastic resin composition which comprises:

(a) 100 parts by weight of a graft resin composition (J) obtained bygraft polymerizing an unsaturated carboxylic acid or a derivativethereof onto a mixture of 1-99% by weight of a polypropylene (C) and99-1% by weight of a rubbery substance (H),

(b) 0.1-600 parts by weight of a saturated polyester resin (F),

(c) 0.1-300 parts by weight of an epoxy group-containing copolymer (G),and

(d) at most 1,900 parts by weight of a polypropylene (C),

the content of the saturated polyester resin (F) in the thermoplasticresin being not more than 50% by weight; and

a thermoplastic resin composition which comprises:

(a) 100 parts by weight of a graft resin composition (K) obtained bygraft polymerizing an unsaturated carboxylic acid or a derivativethereof and an unsaturated aromatic monomer onto a mixture of 1-99% byweight of a polypropylene (C) and 99-1% by weight of a rubbery substance(H),

(b) 0.1-600 parts by weight of a saturated polyester resin (F),

(c) 0.1-300 parts by weight of an epoxy group-containing copolymer (G),and

(d) at most 1,900 parts by weight of a polypropylene (C),

the content of the saturated polyester resin (F) in the thermoplasticresin composition being not more than 50% by weight.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 shows one example of measurement charts in evaluation ofpenetration impact strength, in which the abscissa axis indicates adisplacement amount (D: mm) for deformation of a test piece and theordinate axis indicates a stress (N: newton) to a displacement amount.

A yield point is a point where a stress to a displacement amount changesfrom increment to decrement, and a breaking point is a point where amaterial is fractured and a change in stress disappears.

A yield point energy is an area integration of a displacement amount andstress from a start of stress detection to a yield point of a material,and a total energy is an area integration of a displacement amount andstress from a start to a breaking point.

The polypropylene resin composition (E) used in the present invention isa resin selected out of a graft polypropylene (A) and/or a graftpolypropylene (B), and a composition (D) containing a polypropylene (C)the graft polypropylene (A) and/or the graft polypropylene (B).

The term "polypropylene" will be detailed below.

In the present specification, the term "polypropylene" is used to mean astarting material for the graft polypropylene (A) or the graftpolypropylene (B), or the polypropylene (C).

In the present invention, the "polypropylene" is a crystallinepolypropylene, which includes, besides a polypropylene homopolymer, ablock copolymer obtained by polymerizing propylene at a first step andcopolymerizing the resultant polypropylene with ethylene and an α-olefinsuch as propylene, butene-1, etc., at a second step, and a randomcopolymer obtained by copolymerizing propylene with an α-olefin such asethylene, butene-1, etc.

The polypropylene homopolymer, block copolymer or random copolymer canbe generally produced by polymerization, e.g. in the presence of acombined catalyst of titanium trichloride with an alkyl aluminumcompound which is generally called Ziegler-Natta catalyst.

The polymerization can be carried out at a temperature between 0° C. and300° C. In high-stereoregularity polymerization of an α-olefin such aspropylene, etc., however, a polymer having high stereoregularity cannotbe obtained at a temperature of more than 100° C. For this reason andsome others, the polymerization is carried out preferably at atemperature between 0° C. and 100° C.

The polymerization pressure is not critical, and can be desirablyselected from about 3 to about 100 atmospheric pressures from anindustrial and economical point of view.

The polymerization method may be any of a continuous method and a batchmethod.

The polymerization method can be selected from a slurry polymerizationmethod using an inert hydrocarbon solvent such as butane, pentane,hexane, heptane, octane, or the like, a solvent polymerization method inwhich a resulting polymer is dissolved in one of the inert hydrocarbonsolvents, a solventless bulk polymerization method in which a liquefiedmonomer is polymerized, and a gas phase polymerization method in which agaseous monomer is polymerized.

In order to regulate the molecular weight of the resultant polymer, achain transfer agent such as hydrogen may be added.

The polypropylene used in the present invention can be produced in thepresence of an isospecific Ziegler-Natta catalyst. A catalyst havinghigh isospecificity is preferred.

It is preferred to use a catalyst whose transition metal catalystcomponent is a composite solid compound of a titanium trichloride ormagnesium compound, which have a layer crystalline structure, and atitanium compound and whose typical metal component is an organoaluminumcompound. The catalyst may contain a known electron-donating compound asa third component.

The titanium trichloride is selected from those which are produced byreduction of titanium tetrachloride with a variety of reducing agents.As a reducing agent, there are known metals such as aluminum, titanium,etc., hydrogen, an organometal compound, and the like. A typical exampleof the titanium trichloride produced by metal reduction is a titaniumtrichloride composition containing activated aluminum chloride (TiCl₃AA), produced by reducing titanium tetrachloride with metal aluminum andthen pulverizing the resultant mixture in an apparatus such as a ballmill, a vibration mill, etc. In order to improve isospecificity,polymerization activity and/or particulate properties of the catalyst,the above pulverization may be carried out in the copresence of acompound selected from an ether, a ketone, an ester, aluminum chloride,titanium tetrachloride, etc.

More preferred for the object of the present invention is titaniumtrichloride which is obtained by reducing titanium tetrachloride with anorganoaluminum compound, and catalytically reacting the resultanttitanium trichloride with an ether compound and with a halogen compoundat the same time or consecutively. Preferred is an ether compound whichhas the general formula of R¹ --O--R² (in which each of R¹ and R² is analkyl group having 1 to 18 carbon atoms), and particularly preferred aredi-n-butyl ether and di-t-amyl ether. The halogen compound is selectedpreferably from halogen atoms, iodine in particular; halogen compounds,iodine trichloride in particular; titanium halides, titaniumtetrachloride in particular; and hydrocarbon halides, carbontetrachloride and 1,2-dichloroethane in particular. The organoaluminumcompound has the general formula of AlR³ _(n) X_(3-n) in which R³ is ahydrocarbon group having 1 to 18 carbon atoms, X is a halogen selectedfrom Cl, Br and I, and n is defined by 3≧n>1, and particularly preferredare diethylaluminum chloride and ethylaluminum sesquichloride.

The process for the production of the above titanium trichloride isspecifically disclosed in JP-A-47-34470, JP-A-53-33289, JP-A-53-51285,JP-A-54-11986, JP-A-58-142903, JP-A-60-28405,JP-A-60-228504,JP-A-61-218606, etc.

When titanium trichloride having a layer crystalline structure is usedas a transition metal compound component, it is preferred to use, astypical metal compound component, an organoaluminum compound having thegeneral formula of AlR⁴ _(m) X_(3-m) in which R⁴ is a hydrocarbon grouphaving 1 to 18 carbon atoms, X is a halogen selected from Cl, Br and I,and m is defined by 3≧m>0. Particularly preferred from the object of thepresent invention is an organoaluminum compound of the above generalformula in which R⁴ is an ethyl or isobutyl group and m is defined by2.5≧m>1.5. Specific examples thereof are diethylaluminum chloride,diethylaluminum bromide, diethylaluminum iodide, and mixtures of thesewith either triethylaluminum or ethylaluminum dichloride. When a thirdcompound to be described later is used in combination, preferred for theobject of the present invention is also an organoaluminum compound ofthe, above general formula in which m is defined by 3≧m>2.5or 1.5≧m>0.

The molar ratio of the organoaluminum compound to titanium trichloridecan be selected from the range between 1:1 and 1,000:1.

The catalyst comprising titanium trichloride and organoaluminum maycontain a known third component. Examples of the third component areester compounds such as ε-caprolactam, methyl methacrylate, ethylbenzoate, methyl toluylate, etc.; phosphite esters such as triphenylphosphite, tributyl phosphite, etc.; and phosphoric acid derivativessuch as hexamethylphosphorictriamide, etc.; and the like.

The amount of the third component is to be experimentally determinedwith each of the above compounds, since they differ in activity. Ingeneral, said amount is not more than an equimolar amount to that of theorganoaluminum.

When a composite solid compound of a magnesium compound and a titaniumcompound is used as a transition metal solid catalyst component, it ispreferred to use, as a typical metal catalyst component, anorganoaluminum compound, and it is particularly preferred to use, assuch, a compound having the general formula of AlR⁵ _(p) X_(3-p) inwhich R⁵ is a hydrocarbon group having 1 to 18 carbon atoms, X is ahalogen selected from Cl, Br and I and p is defined by 3≧p>2. Specificexamples thereof are triethylaluminum, triisobutylaluminum and mixturesof these with either diethylaluminum chloride or diisobutylaluminumchloride.

The catalyst also preferably contains an electron-donating compound,particularly an aromatic monocarboxylic acid ester and/or a siliconcompound containing an Si--OR⁶ bond.

As the silicon compound containing an Si--OR⁶ bond, in which R⁶ is ahydrocarbon group having 1 to 20 carbon atoms, preferred is analkoxysilane compound having the general formula of R⁷ _(a)Si(OR⁶)_(4-a) in which each of R⁶ and R⁷ is a hydrocarbon group having 1to 20 carbon atoms and a is defined by 0≦a≦3. Specific examples thereofare tetramethoxysilane, methyltrimethoxysilane, dimethyldimethoxysilane,ethyltrimethoxysilane, phenyltrimethoxysilane, tetraethoxysilane,methyltriethoxysilane, ethyltriethoxysilane, vinyltriethoxysilane,phenyltriethoxysilane, diphenyldimethoxysilane, diphenyldiethoxysilane,butyltriethoxysilane, tetrabutoxysilane, vinyltributoxysilane,diethyldiethoxysilane, etc.

The amount of the above electron-donating compound per mole of theorganoaluminum compound is preferably not more than 1 mole, particularlypreferably 0.05 to 1 mole.

The composite solid compound of a magnesium compound and a titaniumcompound is selected from titanium trichloride containing a chloride ofmagnesium obtained by reducing titanium tetrachloride with anorganomagnesium compound, and the so-called "supported catalyst"prepared by catalytically reacting a solid magnesium compound with aliquid-phase titanium compound. The solid magnesium compound preferablycontains an electron-donating compound, particularly an aromaticmonocarboxylic acid ester, an aromatic dicarboxylic acid diester, anether compound, alcohols and/or phenolic compounds. The aromaticmonocarboxylic acid ester may be co-present when the solid magnesiumcompound is catalytically reacted with the titanium compound.

The above composite solid compound of a magnesium compound and atitanium compound is disclosed in many patent publications, and thosesuitable for the object of the present invention are specificallydisclosed in JP-A-54-112988, JP-A-54-119586, JP-A-56-30407,JP-A-57-59909, JP-A-57-59910, JP-A-57-59911, JP-A-57-59912,JP-A-57-59914, JP-A-57-59915, JP-A-57-59916, JP-A-54-112982,JP-A-55-133408, JP-A-58-27704, etc.

When the thermoplastic resin composition of the present invention isused particularly in fields where heat resistance, stiffness, scratchresistance, etc. are required, it is desirable to use a highlycrystalline polypropylene in which the homopolymer of propylene or thehomopolymer portion as a first segment polymerized in the first step ofblock-copolymerizing propylene has an isotactic pentad of the boilingheptane-insoluble portion of 0.970 or more, a content of the boilingheptane-soluble portion of not more than 5% by weight and a content of20° C. xylene-soluble portion of not more than 2.0% by weight.

The above isotactic pentad of the boiling heptane-insoluble portion, thecontent of the boiling heptane-soluble portion and the content of the20° C. xylene-soluble portion are determined as follows.

5 Grams of a polypropylene was completely dissolved in 500 ml of boilingxylene, and the resultant solution was cooled to 20° C., and allowed tostand for 4 hours. Then, the solution was filtered to separate a 20° C.xylene-insoluble portion. Xylene was evaporated by concentrating thefiltrate and solidifying it by drying, and the residue is further driedunder reduced pressure at 60° C. to obtain a polymer soluble in xyleneat 20° C. The content of the 20° C. xylene-soluble portion is determinedby dividing the dry weight of the polymer by the weight of the chargedsample, and represented by percentage. The above 20° C. xylene-insolubleportion was dried, and then extracted with boiling n-heptane in aSoxhlet apparatus for 8 hours. The extraction residue is referred to asa boiling heptane-insoluble portion, and the content of the boilingheptane-insoluble portion is determined by subtracting the dry weight ofthe boiling heptane-insoluble portion from the weight (5 g) of thecharged sample and dividing the remainder by the weight of the chargedsample, and represented by percentage.

The "isotactic pentad" refers to a fraction of a propylene monomer unitpresent in the central position of an isotactic chain of a polypropylenemolecule chain in a pentad unit or a chain formed of meso-bonded fivesuccessive propylene monomer units, determined by a method disclosed byA. Zambelli et al., in Macromolecules 6, 925 (1973), i.e. a method using¹³ C-NMR. NMR absorption peaks are assigned on the basis of thesubsequently issued Macromolecules 8, 687 (1975).

Specifically, the isotactic pentad is determined on the basis of arelative ratio of the area of mmmm peaks to the total area of theabsorption peaks assigned to methyl carbons. According to this method,the NPL standard substance CRM No. M19-14 Polypropylene PP/MWD/2provided by the National Physical Laboratory in United Kingdom wasmeasured for an isotactic pentad to show 0.944.

The above highly crystalline polypropylene can be prepared by any of themethods disclosed in JP-A-60-28405, JP-A-60-228504, JP-A-61-218606,JP-A-61-287917, etc.

When the thermoplastic propylene resin composition of the presentinvention is used in fields where impact resistance is required, it ispreferred to use, as a polypropylene, a propylene block copolymerproduced by copolymerizing a propylene homopolymer portion, as the firstsegment polymerized in the first step, with ethylene and an α-olefinsuch as propylene, butene-1, etc., as the second segment in the secondstep.

The propylene block copolymer can be prepared by a slurry polymerizationor gas phase polymerization method. In particular, when thethermoplastic resin composition is used in a field where high impactresistance is required, it is required to increase the amount of thesecond segment, and such a propylene block copolymer can be suitablyprepared by a gas phase polymerization method.

Such a polypropylene having a high impact resistance can be prepared bya gas phase polymerization method disclosed, e.g. in JP-A-61-287917.

In the propylene block copolymer, the propylene homopolymer portionpolymerized in the first step may be any of a propylene homopolymer or acopolymer of propylene with ethylene or an α-olefin having 4 to 6 carbonatoms, provided that the content of the ethylene or α-olefin units inthe resultant polymer is not more than 6 mole %. The copolymer portionas the second segment polymerized in the second step is preferably apolymer of ethylene or a copolymer of ethylene, propylene and optionallyan α-olefin having 4 to 6 carbon atoms provided that the ethylenecontent is not less than 10 mole %. The amount of the polymer formed inthe second step is 10 to 70% by weight based on the propylene blockcopolymer.

In a slurry polymerization method, a propylene block copolymer having asecond segment content of 10 to 30% by weight is suitably produced, andin a gas phase polymerization method, a propylene block copolymer havinga second segment content of 10 to 70% by weight is suitably produced.

In the gas phase polymerization method, a propylene block copolymerhaving a larger content of the second segment can be prepared by aprocess disclosed in JP-A-1-98604, and such a copolymer can be suitablyused in a field where ultrahigh impact resistance is required.

The intrinsic viscosity of the second segment in decalin at 135° C.should be changed depending upon the production efficiency, physicalproperties of a product powder and the intrinsic viscosity of the firstsegment. In general, however, the second segment according to a slurrypolymerization method has an intrinsic viscosity of about 3 to 8 dl/g,and the second segment according to a gas phase polymerization methodhas an intrinsic viscosity of i to 5 dl/g.

In the present invention, the graft polypropylene (A) can be obtained bygraft-polymerizing an unsaturated carboxylic acid or a derivativethereof as a graft monomer onto the polypropylene, and the graftpolypropylene (B) can be obtained by graft-polymerizing an unsaturatedcarboxylic acid or a derivative thereof and an unsaturated aromaticmonomer as graft monomers onto the polypropylene, if necessary, in thepresence of a radical initiator.

The above graft monomers can be grafted on the polypropylene accordingto various conventional methods.

For example, the grafting can be carried out by a method which comprisesmixing the polypropylene, the graft monomer(s) and a radical-generatingagent and melt-kneading the resultant mixture in a melt-kneadingapparatus, or by a method which comprises dissolving the polypropylenein an organic solvent such as xylene, adding a radical-generating agentunder nitrogen atmosphere, carrying out a reaction of the resultantmixture by heating it with stirring, cooling the reaction mixture afterthe reaction, washing the reaction product, filtering it and drying it.Besides the above methods, there can be employed a method whichcomprises irradiating the polypropylene with ultraviolet light orradiation in the presence of the graft monomer(s) or a method whichcomprises bringing the polypropylene into contact with oxygen or ozonein the presence of the graft monomer(s).

In view of economical benefit, etc., the most preferred is the graftpolymerization method which comprises melt-kneading the polypropyleneand graft monomer(s) in a melt-kneading apparatus.

The melt-kneading of the polypropylene and an unsaturated carboxylicacid or a derivative thereof, if necessary, in the presence of a radicalinitiator can be carried out with an extruder, a Banbury mixer, akneader, etc. at a temperature of 150° to 300° C., preferably 190° to280° C. for a residence time of 0.3 to 10 minutes, preferably 0.5 to 5minutes. It is industrially advantageous to continuously produce a graftpolypropylene with a single- or twin-screw extruder with keeping thevent holes in a vacuous state and removing unreacted components(unsaturated carboxylic acid or a derivative thereof, unsaturatedaromatic monomer, radical initiator, etc.) and by-products such asoligomers and decomposition products of these components. The reactionmay be carried out in air, but is preferably carried out in an inert gassuch as nitrogen or carbon dioxide. In addition, in order to furtherremove a trace amount of the unreacted components and by-productscontained in the graft polypropylene, the graft polypropylene may beheat-treated at a temperature of 60° C. or higher, extracted with asolvent and vacuumed while it is melted.

A variety of additives may be optionally added to the graftpolypropylene (A) or (B) during the modification or post-treatment.Examples of such additives are an antioxidant, a heat stabilizer, alight stabilizer, a nucleating agent, a lubricant, an anti-static agent,an inorganic or organic colorant, a rust preventive, a crosslinkingagent, a foaming agent, a plasticizer, a fluorescent agent, a surfacetreating agent, a surface brightener, etc.

Examples of the unsaturated carboxylic acid or the derivative thereof,used in the graft polypropylene (A) or (B) are unsaturated carboxylicacids such as acrylic acid, methacrylic acid, maleic acid, itaconicacid, citraconic acid, bicyclo[2,2,1]hepta-5-ene-2,3-dicarboxylic acid(himic acid), bicyclo[2,2,21octa-5-ene-2,3-dicarboxylic acid,4-methylcyclohexa-4-ene-1,2-dicarboxylic acid,1,2,3,4,5,8,9,10-octahydronaphthalene-2,3-dicarboxylic acid,bicyclo[2,2,11octa-7-ene-2,3,5,6-tetracarboxylic acid,7-oxabicyclo[2,2,1]hepta-5-ene-2,3-dicarboxylic acid, etc.; and acidanhydrides, esters, amides, imides and metal salts of the unsaturatedcarboxylic acids such as maleic anhydrides, itaconic anhydride,citraconic anhydrides, bicyclo[2,2,1]hepta-5-ene-2,3-dicarboxylic acidanhydride (himic anhydride), monoethyl maleate, monoethyl fumarate,monomethyl itaconate, monomethyl fumarate, dimethylaminoethylmethacrylate, dimethylaminopropylacrylamide, acrylamide, methacrylamide,maleic acid monoamide, maleic acid diamide, maleicacid-N-monoethylamide, maleic acid-N,N-diethylamide, maleicacid-N-monobutylamide, maleic acid-N,N-dibutylamide, fumaric acidmonoamide, fumaric acid-diamide, fumaric acid-N-monoethylamide, fumaricacid-N,N-diethylamide, fumaric acid-N-monobutylamide, fumaricacid-N,N-dibutylamide, maleimide, N-butylmaleimide, N-phenylmaleimide,sodium acrylate, sodium methacrylate, potassium acrylate, potassiummethacrylate, etc.

Of these, maleic anhydride is most preferred.

The most preferred example of the unsaturated aromatic monomer used inthe graft polypropylene (B) is styrene. Other examples of theunsaturated aromatic monomer are o-methylstyrene, p-methylstyrene,m-methylstyrene, α-methylstyrene, vinyltoluene, divinylbenzene. Thesecompounds may be used in combination.

The graft polypropylene can be produced in the absence of a radicalinitiator. In general, however, it is carried out preferably in thepresence of a radical initiator. The radical initiator can be selectedfrom known radical initiators. Examples of the radical initiator are azocompounds such as 2,2'-azobisisobutyronitrile,2,2'-azobis[2,4,4]-trimethylvaleronitrile, etc.; and various organicperoxides such as methyl ethyl ketone peroxide, cyclohexanone peroxide,3,3,5-trimethylcyclohexanone peroxide, 2,2-bis(t-butylperoxy)butane,t-butyl hydroperoxide, cumene hydroperoxide, diisopropylbenzenehydroperoxide, 2,5-dimethylhexane-2,5-dihydroperoxide, di-t-butylperoxide, 1,3-bis-(t-butylperoxyisopropyl)benzene,2,5-dimethyl-2,5-di(t-butylperoxy)hexane,2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3, lauroyl peroxide,3,3,5-trimethylhexanoyl peroxide, benzoyl peroxide, t-butyl peracetate,t-butylperoxyisobutyrate, t-butyloxypivarate,t-butyloxy-2-ethylhexanoate, t-butylperoxy-3,5,5-trimethylhexanoate,t-butylperoxylaurate, t-butylperoxybenzoate,di-t-butylperoxyisophthalate, 2,5-dimethyl-2,5-di(benzoylperoxy)hexane,t-butylperoxymaleic acid, t-butylperoxyisopropylcarbonate, polystyreneperoxide, etc.

In the production of the graft polypropylene (A) or (B), the melt flowrate of the polypropylenes as a starting material (crystalline propylenehomopolymer, crystalline propylene-ethylene/α-olefin block copolymer,crystalline propylene-ethylene/α-olefin random copolymer, etc.) is notcritical. In general, however, it is 0.05 to 60 g/10 minutes, preferably0.1 to 40 g/10 minutes. Further, it is desirable to selectpolypropylenes as a starting material such that the melt flow rate ofthe resultant modified polypropylene (A) or (B) is 0.1 to 100 g/10minutes, preferably 0.5 to 50 g/10 minutes. The polypropylene as astarting material has usually a number average molecular weight of 7,000to 800,000, preferably 10,000 to 700,000.

In the production of the graft polypropylene (A) or (B), the amount ofeach component per 100 parts by weight of the polypropylene are asfollows. The amount of the unsaturated carboxylic acid or a derivativethereof is preferably 0.01 to 10 parts by weight, more preferably 0.1 to5 parts by weight; that of the unsaturated aromatic monomer is 0.01 to10 parts by weight, more preferably 0.1 to 5 parts by weight; and thatof the radical initiator is preferably 0 to 5 parts by weight, morepreferably 0.001 to 2 parts by weight. When the amount of theunsaturated carboxylic acid or a derivative thereof, or the amount ofthe unsaturated aromatic monomer, is less than 0.01 parts by weight,there is no remarkable effect on the modification. When it exceeds 10parts by weight, the effect on the modification arrives at its limit,and no further effect is exhibited. Moreover, the use of such an excessamount thereof is practically undesirable, since a large amount of sucha component remains unreacted in the resultant polymer, which causesoffensive smell and a degradation in the physical properties of theresultant resin composition. The use of the radical initiator in anamount of more than 5% by weight is practically undesirable, since itgives no further remarkable effect on the graft reaction of theunsaturated carboxylic acid or a derivative thereof and since thepolypropylene is decomposed to a great extent to change the fluidity(melt flow rate) greatly.

In the present invention, the polypropylene resin (E) selected out ofthe graft polypropylene (A), the graft polypropylene (B) and thecomposition (D) of the graft polypropylene (A) and/or the graftpolypropylene (B) with the polypropylene (C) has a melt flow rate,preferably, of 0.1 to 100 g/10 minutes, particularly preferably, of 0.5to 40 g/10 minutes.

In the present invention, the saturated polyester resin (F) is derivedfrom a dicarboxylic acid component of which at least 40 mole % isterephthalic acid and a diol component. The dicarboxylic acid componentother than the above terephthalic acid can be selected from aliphaticdicarboxylic acids having 2 to 20 carbon atoms such as adipic acid,sebacic acid, dodecanedicarboxylic acid, etc.; aromatic dicarboxylicacids such as isophthalic acid, naphthalenedicarboxylic acid, etc.; andalicyclic dicarboxylic acids such as cyclohexanedicarboxylic acid, etc.The compounds may be used alone or in combination. The above diolcomponent can be selected from aliphatic glycols and alicyclic glycolssuch as ethylene glycol, 1,3-propanediol, 1,4-butanediol,1,6-hexanediol, 1,1-decanediol, 1,4-cyclohexanediol, etc.; and thesecompounds may be used alone or in combination.

Of these compounds for the saturated polyester resin (F), polybutyleneterephthalate or polyethylene terephthalate are preferred to exhibit theeffects of the present invention further desirably. The saturatedpolyester resin (F) preferably has an intrinsic viscosity, measured ino-chlorophenol at 25° C., of 0.5 to 3.0 dl/g. When there is used asaturated polyester resin having an intrinsic viscosity outside theabove range as the saturated polyester resin (F), it does not tend to bepossible to achieve the intended mechanical strength.

In the present invention, the epoxy group-containing copolymer (G) is acopolymer composed of an unsaturated epoxy compound and an ethylenicallyunsaturated compound.

The composition ratio of the epoxy group-containing copolymer (G) is notcritical. In general, however, the proportion of the unsaturated epoxycompound is 0.1 to 50% by weight, preferably 1 to 30% by weight.

The unsaturated epoxy compound is a compound containing in the moleculean unsaturated group copolymerizable with an ethylenically unsaturatedcompound and an epoxy group.

Examples of the unsaturated epoxy compound are unsaturated glycidylesters and unsaturated glycidyl ethers which are represented by thefollowing general formulae (1) and (2), respectively. ##STR1##

wherein R is a C₂₋₁₈ hydrocarbon group having an ethylenicallyunsaturated bond. ##STR2##

wherein R is a C₂₋₁₈ hydrocarbon group having an ethylenicallyunsaturated bond, and X is --CH₂ --O-- or ##STR3##

Specific examples of the unsaturated epoxy compound are glycidylacrylate, glycidyl methacrylate, glycidyl itaconates, allylglycidylether, 2-methylglycidyl ether, styrene-p-glycidyl ether.

Examples of the ethylenically unsaturated compound are olefins, vinylesters of a saturated carboxylic acid having 2 to 6 carbon atoms, estersof a saturated alcohol having 1 to 8 carbon atoms with either acrylicacid or methacrylic acid, maleic acid esters, methacrylic acid esters,fumaric acid esters, halogenated vinyls, styrenes, nitriles, vinylethers, acrylamides, etc.

Specific examples of the ethylenically unsaturated compound areethylene, propylene, butene-1, vinyl acetate, methyl acrylate, ethylacrylate, methyl methacrylate, dimethyl maleate, diethyl fumarate, vinylchloride, vinylidene chloride, styrene, acrylonitrile, isobutyl vinylether, acrylamide, etc. Of these, ethylene is particularly preferred.

In order to improve the low-temperature impact resistance by decreasinga glass transition temperature, it is preferable to use vinyl acetateand/or methyl acrylate, etc., as a third component in addition toethylene as a second component.

The epoxy group-containing copolymer can be prepared by various methods.It is possible to employ both at random copolymerization method in whichthe unsaturated epoxy compound is introduced into the main chain of thecopolymer and a graft copolymerization method in which the unsaturatedepoxy compound is introduced as a branch for the copolymer. Thepreparation method can be specifically selected from a method whichcomprises copolymerizing an unsaturated epoxy compound and ethylene inthe presence of a radical-generating agent at 500 to 4,000 atmosphericpressure at 100° to 300° C. in the presence or absence of a suitablesolvent and chain transfer agent, a method which comprises mixing apolypropylene with the unsaturated epoxy compound and aradical-generating agent and subjecting the resultant mixture to meltgraft polymerization in an extruder and a method which comprisescopolymerizing an unsaturated epoxy compound and the ethylenicallyunsaturated compound in an inert medium such as water or an organicsolvent in the presence of a radical-generating agent.

The rubbery substance (H) which is used in the present invention toimprove the impact resistance, low-temperature impact resistance inparticular, can be selected from propylene-butene rubber,isoprene-butylene rubber, polyisoprene, polybutadiene, styrene-basedblock copolymers such as styrene-butadiene rubber, astyrene-butadiene-styrene block copolymer, a partially hydrogenatedstyrene-butadiene block copolymer, styrene-isoprene block copolymer, apartially hydrogenated styrene-isoprene block copolymer, etc., linearlow-density polyethylene, and mixtures of these.

The modified rubbery substance (I) is obtained by graft-polymerizing anunsaturated carboxylic acid or a derivative thereof, or an unsaturatedcarboxylic acid or a derivative thereof and an unsaturated aromaticmonomer, onto the above rubbery substance (I), if necessary, in theco-presence of a radical initiator or by introducing the unsaturatedcarboxylic acid or a derivative thereof, or a mixture of the unsaturatedcarboxylic acid or a derivative thereof with the unsaturated aromaticmonomer, into the α-olefin main chain in the presence of apolymerization initiator or a catalyst.

Of the styrene-based block copolymers, particularly preferred is apartially hydrogenated styrene-butadiene block copolymer. The partiallyhydrogenated styrene-butadiene block copolymer is produced by partialhydrogenation of a styrene-butadiene block copolymer. The structure andproduction process thereof are described below.

As to the partially hydrogenated styrene-butadiene block copolymer, thenumber average molecular weight of the block copolymer rubber is 10,000to 1,000,000, preferably 20,000 to 300,000; the number average molecularweight of the unsaturated aromatic polymer block A in the blockcopolymer rubber is 1,000 to 200,000, preferably 2,000 to 100,000; thenumber average molecular weight of the conjugated diene polymer block Bis 1,000 to 200,000, preferably 2,000 to 100,000; and the weight ratioof the unsaturated aromatic polymer block A to the conjugated dienepolymer block B is 2:98 to 60:40, preferably 10:90 to 40:60.

Many processes have been proposed for the production of the blockcopolymer rubber. A typical process is disclosed in Japanese PatentPublication Kokoku No. 40-23798, in which a block copolymer rubber of anunsaturated aromatic hydrocarbon and a diene hydrocarbon can be producedby block copolymerization in an inert solvents-in the presence of alithium catalyst or a Ziegler-type catalyst.

Such a block copolymer rubber is hydrogenated in an inert solvent in thepresence of a hydrogenation Catalyst, e.g. according to any of themethods disclosed in Japanese Patent Publications Kokoku Nos. 42-8704,43-6636 and 46-20814. The hydrogenation is carried out so that at least50%, preferably 80% or more of the polymer block B is hydrogenated andnot more than 25% of the aromatic Unsaturated bonds in the unsaturatedaromatic polymer is hydrogenated. One typical example of such apartially or completely hydrogenated block copolymer is on the market inthe trade name of KRATON®-G, supplied by Shell Chemical, Ltd., U.S.A.

In the production of the modified rubbery substance (I), the method forgraft-copolymerizing a graft monomer on the rubbery substance can beselected from a variety of known methods.

For example, the graft copolymerization is carried out by a method whichcomprises mixing a rubbery substance as a raw material, a graft monomerand a radical initiator and melt-kneading the mixture in a melt-kneadingapparatus, or a method which comprises dissolving a rubbery substance asa raw material in an organic solvent such as xylene, adding a radicalinitiator under nitrogen atmosphere, allowing the mixture to react underheat with stirring, cooling the reaction mixture after the reaction,washing the reaction product, filtering it and drying it thereby toobtain a grafted rubbery substance. In addition to these, three are amethod which comprises irradiating a rubbery substance as a raw materialwith ultraviolet light or radiation in the presence of a graft monomer,and method which comprises bringing a rubbery substance into contactwith oxygen or ozone.

In view of economical benefit, it is most preferred to employ a graftcopolymerization method in which the above components are melt-kneadedin a melt-kneading apparatus.

In the present invention, the modified rubbery substance (I) can beobtained by melt-kneading a rubbery substance as a raw material with anunsaturated carboxylic acid or a derivative thereof optionally in theco-presence of a radical initiator, or a rubbery substance as a rawmaterial with an unsaturated carboxylic acid or an derivative thereofand an unsaturated aromatic monomer optionally in the co-presence of aradical initiator, with an extruder, Banbury mixer, kneader, or thelike, at a temperature of 200° to 280° C. preferably 230° to 260° C. fora residence time of 0.2 to 10 minutes, which residence time variesdepending upon the radical initiator.

The presence of too large an amount of oxygen during the kneadingsometimes results in formation of a gel or serious coloring. Therefore,the kneading is carried out desirably in the substantial absence ofoxygen.

When the kneading temperature is lower than 200° C., desirably largeamount of unsaturated carboxylic acid anhydride is not grafted, and onlya small effect is produced on improvement in the degree of the graftreaction. When the kneading temperature is higher than 280° C.,undesirably, the effect on improvement in the degree of the graftreaction is small, and in some cases, formation of a gel, coloring,etc., are liable to occur.

The kneading machine is not critical. In general, an extruder ispreferred since it permits continuous production, and the extruderpreferably has a single screw or twin screws suitable for homogeneouslykneading the various raw materials.

In order to remove unreacted components (unsaturated carboxylic acid ora derivative thereof, unsaturated aromatic monomer, radical initiator,etc.) and by-products such as oligomers and decomposition productsthereof from the reaction product, the reaction product can be purifiedby effecting vacuum pump-suction through vent lines halfway along theextruder or at a site near its outlet, or by dissolving the reactionproduct in a suitable solvent to precipitate it. The reaction productcan be also subjected to heat treatment at a temperature of not lessthan 60° C. and suction to vacuum with melting.

The above three or four components may be separately fed to a kneadingmachine, or alternatively, some or all of these components may beuniformly mixed in advance of feeding them. For example, it is possibleto employ a kneading method which comprises impregnating a rubber withboth a radical initiator and an unsaturated aromatic monomer, feedingthe resulting rubber, and the unsaturated carboxylic acid or aderivative thereof at the same time and kneading the resultant mixture.It is also possible to employ a modification method which comprisesfeeding a radical initiator and/or an unsaturated carboxylic acid or aderivative thereof and an unsaturated aromatic monomer halfway along anextruder.

A variety of additives may be optionally added to the modified rubberysubstance (I) during the modification or post-treatment. Examples ofsuch additives are an antioxidant, a heat stabilizer, a lightstabilizer, a nucleating agent, a lubricant, an anti-static agent, aninorganic or organic colorant, a rust preventive, a crosslinking agent,a foaming agent, a plasticizer, a fluorescent agent, a surface treatingagent, a surface brightener, etc.

The unsaturated carboxylic acid or a derivative thereof and the radicalinitiator for use in the modified rubbery substance (I) can be selectedfrom those compounds used for the production of the graft polypropylene(A). As an unsaturated aromatic monomer, styrene is most preferred. Theunsaturated aromatic monomer can be also selected from o-methylstyrene,p-methylstyrene, α-methylstyrene, vinyltoluene, divinylbenzene andmixtures of these.

In the production of said modified rubbery substance (I), theunsaturated aromatic monomer is used to prevent gel formation andimprove the graft reaction degree. Per 100 parts by weight of therubbery substance as a raw material, the amount of the unsaturatedaromatic monomer is preferably 0.2 to 20 parts by weight, and the amountof the unsaturated carboxylic acid or a derivative thereof is preferably0.5 to 15 parts by weight. When the unsaturated aromatic monomer isused, the amount of the unsaturated carboxylic acid or a derivativethereof is preferably 0.5 to 15 parts by weight, and the weight ratio ofunsaturated aromatic monomer to the unsaturated carboxylic acid or aderivative thereof is preferably 0.1 to 3.0, more preferably 0.5 to 2.0.

When the weight ratio of the unsaturated aromatic monomer to theunsaturated carboxylic acid or a derivative thereof is less than 0.1,sometimes no effect is observed on prevention of gel formation andimprovement in degree of the graft reaction. Even when the above weightratio exceeds 3.0, no further effect tends to be expected.

The amount used of the radical initiator depends on its kind andkneading conditions. In general, it can be used in an amount of 0.005 to1.0 part by weight, preferably 0.01 to 0.5 part by weight per 100 partsby weight of the rubber as a raw material. When the amount of theradical initiator is less than 0.005 part by weight, desirably largeamount of the unsaturated carboxylic acid or a-derivative thereof is notgrafted, and an effect of combined use of the unsaturated aromaticmonomer on an increase in an amount of the grafted unsaturatedcarboxylic acid or grafted derivative thereof is small. When the aboveamount exceeds 1.0 part by weight, gel formation is, undesirably, liableto occur.

The modified rubbery substance (I) obtained above preferably contains0.1 to 5% by weight of the grafted unsaturated carboxylic acid or aderivative thereof and 0.1 to 5% by weight of the grafted unsaturatedaromatic monomer and preferably has a Mooney viscosity (ML₁₊₄ 121° C.)of 5 to 120.

The modified rubbery substance (I) is also produced by another method inwhich the unsaturated carboxylic acid or a derivative thereof isintroduced into the main chain of the rubbery substance bycopolymerization in the presence of a polymerization initiator and acatalyst. In general, the modified rubbery substance can be produced bythe following known high-pressure radical copolymerization method. Thatis, it can be produced by copolymerizing ethylene with aradical-polymerizable monomer (comonomer) in the presence of a freeradical-generating agent such as organic peroxide, oxygen, etc. Thecopolymerization is generally carried out at a polymerizationtemperature of 130° to 300° C. under a polymerization pressure of 500 to3,000 kg/cm².

The radical-copolymerizable monomer can be selected from unsaturatedcarboxylic acids such as acrylic acid, methacrylic acid, etc.;esterification products thereof; vinyl esters such as vinyl acetate,etc., and the like. Specific examples of the esterification products ofunsaturated carboxylic acids are methyl acrylate, ethyl acrylate, methylmethacrylate, glycidyl methacrylate, etc. These comonomers can be usedalone or in combination.

The comonomer content in the modified rubbery substance (I) directlypolymerized is usually 0.1 to 40% by weight, preferably 1 to 35% byweight. When the comonomer content is less than 0.1% by weight,sometimes no effect is produced on the modification.

Of these copolymers, those specified as ethylene copolymer rubbers whichare the raw materials for the rubbery substance (H) and the modifiedrubber substance (I) are excluded. Of these, an ethylene-acrylic acidcopolymer and an ethylene-methacrylic acid copolymer are preferred.

Each of the graft resin compositions (J) and (K) is produced byco-modifying a polypropylene and the rubbery substance as raw materialsat the same time by adding an unsaturated carboxylic acid or aderivative thereof or a mixture of an unsaturated carboxylic acid or aderivative thereof with an unsaturated aromatic monomer.

That is, the graft resin compositions (J) and (K) are produced byallowing the polypropylene and the rubbery substance as startingmaterials to be co-present and grafting either an unsaturated carboxylicacid or a derivative thereof or a mixture of an unsaturated carboxylicacid or a derivative thereof with an unsaturated aromatic monomer onthem, optionally, in the presence of a radical initiator according to asimilar method to those described concerning the production of themodified polypropylenes (A) and (B) and the modified rubbery substance(I). When the co-grafting is carried out, a partially hydrogenatedstyrene-butadiene block copolymer is most preferred as a rubberystarting material.

The polypropylene and rubbery substance as starting materials areallowed to be co-present according to various known methods as follows.When these two starting materials are pellets, powders or pulverizedproducts, these materials are fed into a co-modifying apparatus such asan extruder separately or through the same feeding port to allow them tobe co-present in the apparatus, or these materials are preliminarilyuniformly mixed by means of a simple mixing device such as a tumbler,Henschel mixer, etc. When either of these materials is a large solid,these materials are preliminarily melt-kneaded and homogenized with abatch melt-kneading apparatus such as a roll, a kneader, a Banburymixer, etc., and pelletized or pulverized so that they can be easily fedto a co-modifying apparatus.

Steps other than the step of allowing the polypropylene and the rubberysubstance as starting materials to be co-present can be carried out inthe same manner as that used for the production of the modifiedpolypropylenes (A) and (B) or that used for the production of themodified rubbery substance (I), whereby the above materials areco-modified.

In said co-modification, the proportions of the polypropylene and therubbery substance as starting materials can be properly selected.However, it is preferable to determine these proportions on the basis ofthe proportions of the modified polypropylenes (A) and (B) and themodified rubbery substance (I) in the thermoplastic polypropylene resincomposition of the present invention.

When the co-modification is carried out, per 100 parts by weight of thepolypropylene and the rubbery substance in total, the amount of theunsaturated carboxylic acid or a derivative thereof is preferably 0.01to 20 parts by weight, more preferably 0.1 to 5 parts by weight; theamount of the unsaturated aromatic monomer, if the unsaturated aromaticmonomer is used, is 0.01 to 15 parts by weight, more preferably 0.1 to 5parts by weight; the weight ratio of the unsaturated aromatic monomer tothe unsaturated carboxylic acid or a derivative thereof, if thesaturated aromatic monomer is used, is 0.1 to 3.0, more preferably 0.5to 2.0; and the amount of the radical initiator, if necessary, ispreferably 0 to 5 parts by weight, more preferably 0.001 to 2 parts byweight.

In order to disperse the polypropylene and the rubbery substance asstarting materials while dynamically co-modifying them, it is preferableto use a highly efficient melt-kneading apparatus such as a highlyefficient twin-screw extruder, etc.

When producing the thermoplastic polypropylene resin composition of thepresent invention, a filler (L) can be incorporated for the purpose ofreinforcement, function impartation and extension (cost-reduction).

The filler (L) can be selected from fibers such as glass fibers, carbonfibers, polyamide fibers, metal fibers, e.g. fibers of aluminum,stainless steel, etc., metal whiskers, etc., and inorganic such assilica, alumina, calcium carbonate, talc, mica, clay, kaolin, carbonblack, TiO₂, ZnO, Sb₂ O₃, etc.

All of these fillers can be used for reinforcement. Fillers such ascarbon fibers, metal fibers, carbon black, etc., can lower the surfaceresistivity and the volume resistivity and impart electricalconductivity to the thermoplastic polypropylene resin composition of thepresent invention. Any filler that is less expensive than the resin canbe used as an extender to reduce the cost.

For the purpose of improvement of the thermoplastic polypropylene resincomposition in stiffness and heat resistance, it is particularlypreferred to select the filler (L) from inorganic fillers such as glassfibers, a potassium titanate whisker, talc, mica, potassium carbonate,etc., and carbon fibers.

It is one of preferred embodiments to use the thermoplasticpolypropylene-based resin composition of the present invention as acomposite material by further incorporating thereinto a flame-retardantor flame retardant auxiliary, a lubricant, a nuclear agent, aplasticizer, a dye, a pigment, an antistatic agent, an antioxidant, aweatherability-imparting agent, etc.

The polypropylene resin/saturated polyester resin composition in thethermoplastic polypropylene resin composition of the present inventioncontains 1 to 99% by weight, preferably 20 to 98% by weight of thepolypropylene resin (E) as a first component. When the content of thepolypropylene resin is less than 1% by weight, the resultantthermoplastic resin composition is not sufficient in moldingprocessability, toughness, water resistance, chemical resistance, etc.

When the composition containing the graft polypropylene (A) and/or thegraft polypropylene (B) and the polypropylene (C) is used as apolypropylene (E), the content of the graft polypropylene (A) and/or thegraft polypropylene (B) in this composition is required to be not lessthan 5% by weight. When said content is less than 5% by weight, thefinal resin composition has a problem in compatibility anddispersibility. Further, no sufficient toughness and impact resistancecan be obtained, nor are the coating properties and printabilitysufficient.

The content of the saturated polyester resin (F) in the thermoplasticpolypropylene resin composition of the present invention is less than50% by weight, preferably 45 to 1% by weight. The saturated polyesterresin (F) produces an effect on improvement in heat resistance,stiffness, strength, etc. When the above content is more than 50% byweight, no desirable properties can be obtained with regard to moldingprocessability, toughness, water resistance, chemical resistance, etc.Further, there are also problems in that the resultant resin compositionhas high specific gravity and is expensive.

The amount of the epoxy group-containing copolymer (G) per 100 parts byweight of the resin composition composed of the polypropylene resin (E)and the saturated polyester resin (F) is 0.1 to 300 parts by weight,preferably 1 to 200 parts by weight. When this amount is less than 1part by weight, the resultant resin composition is sometimes poor incompatibility and dispersibility, and it exhibits insufficient toughnessand impact resistance and poor extrusion stability. The thermoplasticresin composition containing more than 100 parts by weight of the epoxygroup-containing copolymer (G) is useful as an elastomer. However, whenthe above amount exceeds 300 parts by weight, the resultant resincomposition shows great degradation in toughness, heat resistance, etc.,and no desirable result can be obtained.

The amount of the rubbery substance (H) and/or the modified rubberysubstance (I), which are used to improve the impact resistance,low-temperature impact resistance in particular, is 0.1 to 300 parts byweight, preferably 1 to 200 parts by weight per 100 parts by weight ofthe thermoplastic resin composition comprising the polypropylene resin(E) and the saturated polyester resin (F). When this amount is less than0.1 part by weight, no effect is produced on the impact resistance. Thethermoplastic resin composition containing more than 100 parts by weightof the rubbery substance (H) and/or the modified rubbery substance (I)is useful as an elastomer. However, when the above amount exceeds 300parts by weight, the resultant resin composition shows great degradationin toughness, heat resistance, etc., and no desirable result can beobtained.

In the graft resin composition (J) or (K) in the thermoplastic propyleneresin composition of this invention, a mixture of 1 to 99% by weight,preferably 20 to 98% by weight of the polypropylene (C) with 99 to 1% byweight, preferably 98 to 20% by weight of the rubbery substance (H) isgraft-polymerized with the unsaturated carboxylic acid or a derivativethereof in the case of (J) or with the unsaturated carboxylic acid or aderivative thereof and the unsaturated aromatic monomer in the case of(K). When the amount of the rubbery substance (H) is less than 1% byweight, no effect is produced on improvement in impact resistance, andwhen the amount of the polypropylene (C) is less than 1% by weight, theresultant resin composition shows insufficient molding properties,toughness, water resistance and chemical resistance.

The amount of the polypropylene (C) per 100 parts by weight of the graftresin composition (J) or (K) is 0 to 1,900 parts by weight. The amountof the graft polypropylene contained in the graft resin composition (J)or (K) is required to be not less than 5% by weight based on the totalamount of the graft polypropylene and the polypropylene (C) contained inthe graft resin composition (J) or (K). When this amount is less than 5%by weight, the final resin composition shows poor compatibility anddispersibility, and no sufficient toughness and impact resistance can beobtained. Nor are coating properties, adhesive properties andprintability sufficient.

The saturated polyester resin is incorporated in an amount that is 0.1to 600 parts by weight, preferably 2 to 500 parts by weight per 100parts by weight of the graft resin composition (J) or (K). The contentof the saturated polyester resin based on the thermoplastic resincomposition as a whole is less than 50% by weight, preferably 45 to 1%by weight. When this content is more than 50% by weight, no desirableproperties can be obtained with regard to molding properties, toughness,water resistance and chemical resistance. Further, the epoxygroup-containing copolymer (G) is incorporated in an amount of 0.1 to300 parts by weight, preferably 1 to 200 parts by weight. When thisamount is less than 0.1 part by weight, the resultant resin compositionis poor in compatibility and dispersibility, and it exhibitsinsufficient toughness and impact resistance and poor extrusionstability. The thermoplastic resin composition containing more than 100parts by weight of the epoxy group-containing copolymer (G) is useful asan elastomer. However, when the above amount exceeds 300 parts byweight, the resultant resin composition shows great degradation intoughness, heat resistance, etc., and no desirable result can beobtained.

The amount of the filler (L), which is used for reinforcement, functionimpartation or extension (cost-reduction) in the thermoplastic propyleneresin composition of the present invention, is 0.01 to 300 parts byweight, preferably 1 to 200 parts by weight per 100 parts by weight ofthe thermoplastic resin composition comprising the polypropylene resin(E), the saturated polyester resin (F), the epoxy group-containingcopolymer (G) and the rubbery substance (H) and/or the modified rubberysubstance (I) or the thermoplastic resin composition comprising thegraft resin composition (J) or (K), the saturated polyester resin (F)and the epoxy group-containing copolymer (G).

When the above amount is less than 0.01 part by weight, no fillingeffect can be obtained. When it is more than 300 parts by weight, theresultant resin composition shows degradation in toughness and impactresistance. And, properties inherent to the resins are lost and theresultant resin composition is brittle. Thus, no desirable result can beobtained.

The process for the production of the thermoplastic polypropylene resincomposition of the present invention is not critical, and conventionalprocesses can be applied.

It may be effective to employ a process which comprises mixing thestarting materials in a solution state and evaporating a solvent orprecipitating the resin composition in a non-solvent. From an industrialviewpoint, it is preferred to employ a process which comprises kneadingthe starting materials in a molten state. The melt-kneading can becarried out by means of a variety of kneading apparatus such as aBanbury mixer, an extruder, a roll, a kneader, etc.

For the melt-kneading, it is preferable to preliminarily mix the resincomponents all in a powder or pellet form uniformly with an apparatussuch as a tumbler or a Henschel mixer. If necessary, it is possible toindividually feed predetermined amount of the resin components to akneading apparatus without the preliminary mixing.

The kneaded resin composition is molded by various molding methods suchas injection molding, extrusion molding, etc. The scope of the presentinvention also includes the composition obtained by a method in which amolded article is produced by dry-blending the starting materials duringinjection molding or extrusion molding without carrying out thepreliminary mixing step, and kneading the resultant composition duringmelt processing.

In the present invention, the kneading order is not critical: The graftpolypropylene (A) and/or the graft polypropylene (B), the polypropylene(C), the saturated polyester resin (F), the epoxy group-containingcopolymer (G), the rubbery substance (H) and/or the modified rubberysubstance (I), and optionally, the filler (L) may be kneaded in one lot;The polypropylene resin (E) is preliminary prepared by kneading thegraft polypropylene (A) and/or the graft polypropylene (B), or acomposition containing the graft polypropylene (A) and/or the graftpolypropylene (B) and the polypropylene (C), and thereafter, and thesaturated polyester resin (F), the epoxy group-containing copolymer (G),the rubbery substance (H) and/or the modified rubbery substance (I) andoptionally the filler (L) may be added to, and kneaded with, thepolypropylene resin (E); The polypropylene resin (E) and the saturatedpolyester resin (F) may be preliminarily kneaded, and thereafter, theepoxy group-containing copolymer (G), the rubbery substance (H) or themodified rubbery substance (I) and optionally, the basic compound (H)may be added to, and kneaded with, the polypropylene resin (E); and someother kneading orders may be selected. However, when the graftpolypropylene (A) and/or the polypropylene (B) and the epoxygroup-containing copolymer (G), the epoxy group-containing copolymer (G)and the modified rubbery substance (I), or the saturated polyester resin(F) and the epoxy group-containing copolymer (G) are preliminarykneaded, a gel is sometimes formed depending upon proportions of thesetwo components. In such a case, it is necessary to select suitableproportions of the two components properly before the preliminarykneading of them.

The kneading order for the thermoplastic resin composition comprisingthe graft resin composition (J) formed by graft polymerization with theunsaturated carboxylic acid or a derivative thereof or the graft resincomposition (K) formed by graft polymerization with the unsaturatedcarboxylic acid or a derivative thereof and the unsaturated aromaticmonomer in place of the graft polypropylene (A) and/or the graftpolypropylene (B) and the modified rubbery substance (I) may bedetermined in the same way as above.

In order to simplify the kneading step, the step for the preliminaryproduction of the graft resin composition (J) or (K) may be integratedinto the kneading step for the thermoplastic propylene resin compositionof the present invention.

That is, the thermoplastic resin composition of the present inventionmay be produced by co-modifying a polypropylene and a rubbery substanceas starting materials in a first step, and charging the polypropylene(C), the saturated polyester resin (F), the epoxy group-containingcopolymer (G) and optionally, the filler (L) to a site where themodified material or the co-modified materials are in a molten state ina second step.

In order to produce the thermoplastic polypropylene resin composition ofthe present invention more effectively, it is preferred to use a highlyefficient twin-screw extruder having a high L/D ratio and two or morefeeding port. That is, the materials for the co-modification are chargedthrough a first feeding port, and co-modified sufficiently untilcomponents other than the graft polypropylenes (A) and (B) and therubbery substance (H) are charged through a next feeding port, and then,the other components are charged through a second feeding port to kneadthe resultant mixture, whereby the composition can be efficientlyproduced.

The kneading may be carried out in a variety of methods in order toallow the thermoplastic propylene resin composition of the presentinvention to exhibit desired physical properties: In order to have theimpact resistance exhibited efficiently, part of the epoxygroup-containing copolymer (G) is preliminarily kneaded with thesaturated polyester resin and the remaining components are added to, andkneaded with, the kneaded mixture; In order to have the stiffness andheat resistance exhibited efficiently under reinforcement with thefiller (L), the filler (L) is preliminarily kneaded with one resin whichcan well disperse the filler (L) and constitutes the thermoplasticpolypropylene resin composition of the present invention, and then theremaining components are added to, and kneaded with, the resultantkneaded mixture, or alternatively, the filler (L) is charged halfwayalong an extruder while the resin composition is in a preliminary meltedand kneaded state and the resultant mixture is kneaded; and some othermethods.

The thermoplastic resin composition of the present invention can bemolded by a general molding or forming method such as injection molding,extrusion molding, compression molding, blow molding, roll molding,lamination molding, vacuum forming, pressure molding, etc. The presentinvention includes, in its scope, a method in which the components aredry-blended during injection molding or extrusion molding without a stepof preliminary kneading, and the resultant dry blend is kneaded duringmelt-processing.

Of the above molding and forming methods, an injection molding method ispreferred from the viewpoint of productivity, etc. A-molded article isobtained by preliminarily drying a pelletized composition in a vacuumdryer, a hot air dryer, etc., and injection-molding the compositionunder predetermined conditions including injection rate, injection time,cooling temperature, etc.

The present invention will be explained hereinafter by reference toExamples, to which the present invention shall not be limited.

Methods for measuring the physical properties in Examples are describedbelow.

(1) Specific Gravity

Measured according to the method specified in JIS K6758.

(2) Melt Flow Rate

Measured according to the method specified in JIS K6758. The measurementtemperature was 230° C., and the load was 2.16 kg unless otherwisespecified.

(3) Tensile Test

Carried out according to the method specified in ASTM D638. A test piecehaving a thickness of 3.2 mm was measured for a tensile yield strengthand a tensile elongation. The measurement temperature was 23° C. unlessotherwise specified.

(4) Flexural Test

Carried out according to the method specified in JIS K7203. A test piecehaving a thickness of 3.2 mm was measured for a flexural modulus and aflexural strength at a span length of 50 mm at a loading rate of 1.5mm/minute. The measurement temperature was 23° C. unless otherwisespecified. When the test was carried out at a temperature other than 23°C., a sample was conditioned in a constant temperature bath at apredetermined temperature for 2 hours before the test.

(5) Izod Impact Strength

Measured according to the method specified in JIS K7110. A test piecehaving a thickness of 3.2 mm was measured for a notched impact strength.The measurement temperature was 23° C. unless otherwise specified. Whenthe measurement was carried out at a temperature other than 23° C., asample was conditioned in a constant temperature bath at a predeterminedtemperature for 2 hours before the measurement.

(6) Penetration Impact Strength

A high rate impact tester (RIT-8000, supplied by Rheometrics Inc.(U.S.A.)) was used. A deformation degree and stress of a flat test piecehaving a thickness of 3 mm were detected by fixing the test piece with a2-inch circular holder and hitting a 5/8-inch impact probe (tipspherical surface: 5/16 inch Radius) against the test piece at a rate of3 m/second, and a curve was prepared as shown in FIG. 1 on the basis ofthe resultant measurement values. The penetration impact strength wasevaluated by integrating the area along the curve.

One example of measurement charts in evaluation of penetration impactstrength is shown in FIG. 1, in which the abscissa axis indicates adisplacement amount (D: mm) showing deformation of the test piece andthe ordinate axis indicates a stress (N: newton) to a displacementamount. Both of these values were continuously detected and continuouslyplotted in an X-Y plotter whereby said measurement chart was obtained.

A yield point energy was obtained by integrating areas of thedeformation amount and the stress from a start of stress detection to ayield of a material, and a total energy was obtained by integratingareas of the displacement amount and the stress from a start portion toa fracture point.

The fracture state of a material was determined to be ductile fracture(D) or brittle fracture (B) by observing a test piece actually subjectedto a fracture test.

An energy value required for yield of a material was evaluated in termsof energy at a yield point, and an energy value required for fracture ofa material was evaluated in terms of total energy, and these values areshown in a unit of joule (J).

A sample was conditioned in a constant temperature bath attached to theapparatus. A test piece was placed in the constant temperature bathadjusted to a predetermined temperature and conditioned for 2 hoursbefore the above test. The predetermined temperature was used as ameasurement temperature.

(7) Heat Distortion Temperature

Measured according to the method specified in JIS K7207. The fiberstress was measured at 4.6 kg/cm².

(8) Rockwell Hardness

Measured according to the method specified in JIS K7207. The thicknessof a test piece was 3.2 mm, Radius was used as a steel ball, and theevaluation value was expressed on R scale.

(9) Graft Amount of Maleic Anhydride and Styrene

The graft amount of maleic anhydride on the graft polypropylene (A) wasdetermined by dissolving a small amount of a sample in hot xylene,forming a precipitate with anhydrous acetone to purify the sample, thenredissolving the purified sample in xylene, and titrating the resultantsolution with a methanol solution of NaOH while the solution was underheat (110° to 120° C.), and phenolphthalein was used as an indicator.

The graft amount of the maleic anhydride in the modified rubberysubstance (G) was determined by dissolving a small amount of a sample intoluene, forming a precipitate with anhydrous acetone to purify thesample, then redissolving the purified sample in toluene, and titratingthe resultant solution with a ethanol solution of KOH while the solutionwas under heat (85° C.), and phenolphthalein was used as an indicator.The graft amount of styrene was determined on the basis of intensity ofan absorption peak derived from substituted benzene rings observed in aninfrared absorption spectrum of the above purified sample.

(10) Number Average Molecular Weight

Measured by gel permeation chromatography (GPC) under the followingconditions.

GPC: type 150C, supplied by Waters.

Column: Shodex 80 MA, supplied by Showa Denko K.K.

Sample amount: 300 μl (polymer concentration: 0.2 wt %)

Flow rate: 1 ml/min.

Temperature: 135° C.

Solvent: Trichlorobenzene

A calibration curve for calculation of the number average molecularweight was prepared by a conventional method using standard polystyrenesupplied by TOSOH Corp. A data processor CP-8 Model III supplied byTOSOH Corp was used for data processing.

(11) Ethylene Content

The ethylene content was determined by preparing a press sheet,measuring it for an infrared absorption spectrum, and using acalibration curve from absorbances of characteristic absorptions ofmethyl (--CH₃) and methylene (--CH₂ --) which were observed in theinfrared absorption spectrum.

The test pieces for determining the above physical properties wereprepared under the following injection molding conditions unlessotherwise specified. Compositions were dried in a hot-air dryer at 120°C. for 2 hours and injection-molded with an injection molding machine,model IS150E-V, supplied by Toshiba Machinery Co., Ltd. at a moldingtemperature of 240° C. and a mold-cooling temperature of 70° C. for aninjection time of 15 seconds and a cooling time of 30 seconds.

Compositions described below were produced under the followingconditions unless otherwise specified. A predetermined amount of each ofthe components for the compositions was weighed, and the components werepreliminarily mixed uniformly with a Henschel mixer, and then kneaded ina twin-screw continuous kneading machine (model TEX SS 30BW-2V, suppliedby Japan Steel Works Ltd.) at an extrusion rate of 30 kg/hour, a resintemperature of 240° C. and a screw revolution rate of 350/minute whilesuction was carried out through a vent. The screws were composed of twosets of a triple-thread rotor and a triple-thread disc which were placedin two kneading zones, i.e., one zone next to a first feed opening andthe other zone next to a second feed opening.

EXAMPLES 1-3 AND COMPARATIVE EXAMPLES 1 to 2

A graft polypropylene (A) was prepared in the following manner. Apropylene homopolymer which was a starting material prepared by a slurrypolymerization method according to the process described inJP-A-60-28405, and which had a melt flow rate of 1.3 g/10 minute, anintrinsic viscosity, measured in tetralin at 135° C., of 2.45 dl/g, a20° C. cold xylene-soluble content of 2.9% by weight, a boilingheptane-soluble content of 6.7% by weight, and an isotactic pentad, inits boiling heptane-insoluble portion, of 0.955 was modified in thefollowing manner.

100 Parts by weight of the propylene homopolymer as a starting material,1.0 part by weight of maleic anhydride, 0.6 part by weight of a radicalinitiator prepared by allowing a propylene homopolymer to support 8% byweight of 1,3-bis(t-butylperoxyisopropyl)benzene (Sanperox®-TY1-3supplied by Sanken Kako Co., Ltd.) and 0.1 part by weight of Irganox®1010 (supplied by Ciba Geigy, Ltd.) as a stabilizer were uniformly mixedwith a Henschel mixer. The resultant mixture was melt-kneaded with atwin-screw extruder, model TEX 44 SS-30BW-2V supplied by Japan SteelWorks Ltd., at a temperature of 220° C. for an average residence time of1.5 minutes to give a maleic anhydride-grafted polypropylene (A) havinga maleic anhydride graft amount of 0.08% by weight and a melt flow rateof 36 g/10 minutes. This graft polypropylene (A) is abbreviated asM-PP-1 hereinafter. Polybutylene terephthalate (Tafpet PBT® N1000,supplied by Mitsubishi Rayon Co., Ltd.) was used as a saturatedpolyester resin (F). This polybutylene terephthalate as a startingmaterial is abbreviated as PBT-1 hereinafter.

An epoxy group-containing copolymer (G) was prepared in the followingmanner. A terpolymer having a melt flow rate of 21 g/10 minutes (190°C., load: 2.16 kg) and having an ethylene/methyl methacrylate/glycidylmethacrylate weight ratio of 64/14/22 (% by weight) was prepared by ahigh-pressure radical polymerization method according to the processdescribed in JP-A-47-23490 and JP-A-48-11888. This epoxygroup-containing copolymer is abbreviated as E-MA-GMA-1 hereinafter.

A modified rubbery substance (I) was prepared in the following manner.100 Parts by weight of a styrene-ethylene-butylene-styrene blockcopolymer rubber (Kraton®-G1657, supplied by Shell Chemical, Ltd.)having a number average molecular weight of 50,000, a number averagemolecular weight, in its styrene block, of 35,000 and a styreneblock/ethylene block weight ratio of 30/70, 1.0 part of maleicanhydride, and 1.0 part by weight of a radical initiator prepared byallowing a propylene homopolymer to support 8% by weight of1,3-bis(t-butylperoxyisopropyl)benzene (Sanperox®-TY1.3 supplied bySanken Kako Co., Ltd.) were uniformly mixed with a Henschel mixer, andthe resultant mixture was melt-kneaded in a twin-screw extruder, TEX 44SS 30BW-2V,.supplied by Japan Steel Works Ltd., under nitrogenatmosphere at a kneading temperature of 250° C. and an extrusion rate of30 kg/hour to give a modified styrene-ethylene-butylene-styrene blockcopolymer rubber having a maleic anhydride graft amount of 0.38% byweight.

This modified styrene-ethylene-butylene-styrene copolymer rubber isabbreviated as M-SEBS-1 hereinafter.

The above starting materials were mixed in such a manner that theproportions of M-SEBS-1 and E-MA-GMA-1 were constant and those of M-PP-1and PBT-1 were changed as shown in Table 1, and compositions wereproduced under predetermined conditions. Test pieces were prepared fromthe compositions under predetermined injection conditions, and evaluatedaccording to the foregoing methods. Table 1 shows the results of theevaluation of the physical properties of the test pieces.

Although Izod impact strength is generally employed for impactresistance evaluation, there are many substances having high penetrationimpact strength even if their Izod impact strength is low. Polybutyleneterephthalate has a lower notched Izod impact strength at -30° C. thandoes a propylene-ethylene-propylene block copolymer but has a remarkablyhigher penetration impact strength than does the above block copolymer.An actual service of some automobile parts is evaluated bylow-temperature ball dropping test, and this actual service evaluationand a laboratory test on the penetration impact strength give wellconsistent results. In evaluation of the penetration impact strength, atest piece exhibiting a higher energy at yield point and higher totalenergy is rated to be better. The energy at yield point and the totalenergy are calculated from the measurement chart. Further, the fracturestate of a test piece at a fracture point is important for associationof the penetration impact strength with the actual service evaluation.

The fracture state cannot be determined from the measurement chart, butis judged by observing a fracture state of a test piece. A fracturestate in which a sharp crack is formed or a test piece is divided intoseveral pieces is referred to as "brittle fracture". A fracture state inwhich a test piece is fractured along the shape of an impact probewithout formation of a sharp crack and division into several pieces isreferred to as "ductile fracture". A composition which exhibits theductile fracture is preferable to one which exhibits the brittlefracture.

Table 2 shows that the test pieces obtained in Examples 1 to 4 of thepresent invention exhibit a far more improved Izod impact strength andpenetration impact strength than those test pieces of ComparativeExamples 1 and 2 which does not contain any modifiedstyrene-ethylene.butylene-styrene block copolymer rubber.

EXAMPLES 5 AND 6

A modified rubbery substance was prepared in the following manner. 100Parts by weight of the same Kraton®-G 1657 (supplied by Shell Chemical,Ltd.) as that used in Example 1, 1.0 part by weight of maleic anhydride,0.5 part by weight of styrene and 0.6 part by weight of a radicalinitiator were treated in the same manner as in Example 1, whereby therewas produced a modified styrene-ethylene-butylene block copolymer rubberhaving a maleic anhydride graft amount of 0.42% by weight.

The above modified styrene-ethylene-butylene-styrene copolymer rubber isabbreviated as MS-SEBS-1 hereinafter.

A composition was prepared by using the same starting materials as thosein Example 2 in proportions as shown in Table 1 under the predeterminedkneading conditions except for the use of the above MS-SEBS-1 as amodified rubbery substance (I). A test piece was prepared from thecomposition under the predetermined injection conditions, and physicalproperties of the test piece were evaluated according to thepredetermined evaluation methods. Table 2 shows the results of thephysical property evaluation.

EXAMPLE 7

A composition was prepared under the predetermined kneading conditionsby using the same starting materials as those in Example 4 inproportions as shown in Table 1 except that the same Kration®-G 1657 asthat used in Example 1 was used without modifying it. A test piece wasprepared from the composition under the predetermined injectionconditions, and physical properties of the test piece were evaluatedaccording to the predetermined evaluation methods. Table 2 shows theresults of the physical property evaluation.

EXAMPLE 8

An epoxy group-containing copolymer (G) was prepared in the followingmanner. A terpolymer having a melt flow rate of 7 g/10 minutes (190° C.,load 2.16 kg) and having an ethylene/vinyl acetate/glycidyl methacrylateweight ratio of 85/5/10 (% by weight) was prepared by a high-pressureradical polymerization method according to the process described inJP-A-47-23490 and JP-A-48-11888. This epoxy group-containing copolymeris abbreviated as E-VA-GMA-1 hereinafter.

A composition was prepared in the same way as in Examples 1 to 4 byusing the same starting materials as those in Example 5 in proportionsas shown in Table 1 except that E-VA-GMA-1 was used as an epoxygroup-containing copolymer (G). Table 2 shows the results of thephysical property evaluation.

EXAMPLE 9

A graft polypropylene (B) was prepared in the following manner. Apropylene homopolymer which was a starting material prepared by a slurrypolymerization method according to the process described inJP-A-60-28405, and which had a melt flow rate of 1.3 g/10 minutes, anintrinsic viscosity, measured in tetralin at 135° C., of 2.45 dl/g, a20° C. cold xylene-soluble content of 2.9% by weight, a boilingheptane-soluble content of 6.7% by weight, and an isotactic pentad, inits boiling heptane-insoluble portion, of 0.955 was modified in thefollowing manner.

100 Parts by weight of the propylene homopolymer as a starting material,1.0 part by weight of maleic anhydride, 0.5 part by weight of styrene,0.6 part by weight of a radical initiator prepared by allowing apropylene homopolymer to support 8% by weight of1,3-bis(t-butylperoxyisopropyl)benzene (Sanperox®-TY1-3 supplied bySanken Kako Co., Ltd.) and 0.1 part by weight of Irganox® 1010 (suppliedby Ciba Geigy, Ltd.) as a stabilizer were uniformly mixed with aHenschel mixer. The resultant mixture was melt-kneaded with a twin-screwextruder, model TEX 44 SS-30BW-2V supplied by Japan Steel Works Ltd., ata temperature of 220° C. for an average residence time of 1.5 minutes togive a maleic anhydride.styrene-grafted polypropylene (B) having amaleic anhydride graft amount of 0.15% by weight, a styrene graft amountof 0.07% by weight and a melt flow rate of 21 g/10 minutes. This graftpolypropylene (B) is abbreviated as MS-PP-1 hereinafter.

A composition was prepared in the same way as in Examples 1 to 4 byusing the same proportion of the same starting materials as those inExample 1 except that graft polypropylene MS-PP-1 was used in place ofthe graft polypropylene (A). Table 2 shows the results of the physicalproperty evaluation.

EXAMPLE 10

A composition was prepared in the same way as in Examples 1 to 4 byusing the same proportion of the same starting materials as those inExample 5 except that MS-PP-1 was used as a graft polypropylene (B).Table 2 shows the results of the physical property evaluation.

EXAMPLE 11

A composition was prepared in the same way as in Examples 1 to 4 byusing the same proportion of the same starting materials as those inExample 6 except that graft polypropylene MS-PP-1 was used as a graftpolypropylene (B). Table 2 shows the results of the physical propertyevaluation.

EXAMPLE 12

A composition was prepared in the same way as in Example 1 except that acografted product of M-PP-1 and M-SEBS-1 as a graft resin composition(J) was used in place of the M-PP-1 and M-SEBS-1. 100 Parts by weight ofa composition obtained by mixing a polypropylene powder as a startingmaterial for M-PP-1 with pellets of a styrene-ethylene-butylene-styreneblock copolymer rubber as a material for M-SEBS-1 in a mixing ratio of70/15, 1.0 part by weight of maleic anhydride, 0.6 part by weight of aradical initiator prepared by allowing a propylene homopolymer tosupport 8% by weight of 1,3-bis(t-butylperoxyisopropyl)benzene(Sanperox®-TY1-3 supplied by Sanken Kako Co., Ltd.) and 0.1 part byweight of Irganox® 1010 (supplied by Ciba Geigy) as a stabilizing wereuniformly mixed with a Henschel mixer. The resultant mixture wasmelt-kneaded with a twin-screw extruder, model TEX 44 SS-30BW-2Vsupplied by Japan Steel Works Ltd., at a temperature of 220° C. for anaverage residence time of 1.5 minutes to give a maleicanhydride-cografted polypropylene/styrene-ethylene-butylene-styreneblock copolymer rubber having a maleic anhydride graft amount of 0.13%by weight and a melt flow rate of 15 g/10 minutes. This co-modifiedproduct is abbreviated as M-(PP/SEBS)-1 hereinafter.

A composition was prepared in the same way as in Example 1 except thatthe co-modified product M-(PP/SEBS)-1 was used, and physical propertiesthereof were evaluated. Table 2 shows the results of the physicalproperty evaluation.

A test piece prepared from the above composition containing theco-modified product M-(PP/SEBS)-1 exhibited as excellent Izod impactstrength and penetration impact strength as those of the test piece ofExample 1 prepared from the composition containing the individuallymodified products M-PP-1 and M-SEBS-1.

EXAMPLE 13

A graft resin composition (J) was prepared by repeating the sameprocedure as in Example 12 except that the polypropylenepowder/styrene-ethylene.butylene-styrene block copolymer rubber weightratio was changed to 55/20, whereby a maleic anhdyride-cograftedpolypropylene/styrene-ethylene.butylene-styrene block copolymer rubberwas obtained. This graft product is abbreviated as M-(PP/SEBS)-2hereinafter.

A composition was prepared in the same way as in Example 4 except thatthe cografted product M-(PP/SEBS)-2 was used as shown in Table 1, andphysical properties thereof were evaluated. Table 2 shows the results ofthe physical property evaluation.

A test piece prepared from the above composition containing thecografted product M-(PP/SEBS)-2 exhibited as excellent Izod impactstrength and penetration impact strength as those of the test piece ofExample 4 prepared from the composition containing the individuallymodified products M-PP-1 and M-SEBS-1.

EXAMPLES 14 AND 15

A composition was prepared in the same way as in Example 10 except thata cografted product of MS-PP-1 and MS-SEBS-1 as a co-graft resincomposition (K) was used in place of MS-PP-1 and MS-SEBS-1.

100 Parts by weight of a composition prepared by mixing a polypropylenepowder as a starting material for MS-PP-1 with pellets of astyrene-ethylene.butylene-styrene block copolymer rubber as a startingmaterial for MS-SEBS-1 in a mixing ratio of 70/15 or 55/20, 1.0 part byweight of maleic anhydride, 0.5 part by weight of styrene, 0.6 part byweight of a radical initiator prepared by allowing a propylenehomopolymer to support 8% by weight of1,3-bis(t-butylperoxyisopropyl)benzene (Sanperox®-TY1-3 supplied bySanken Kako Co., Ltd.) and 0.1 part by weight of Irganox® 1010 (suppliedby Ciba Geigy, Ltd.) as a stabilizer were uniformly mixed with aHenschel mixer. The resultant mixture was melt-kneaded with a twin-screwextruder, model TEX 44 SS-30BW-2V supplied by Japan Steel Works Ltd., ata temperature of 220° C. for an average residence time of 1.5 minutes togive a maleic anhydride-styrene-cograftedpolypropylene/styrene-ethylene.butylene-styrene block copolymer rubberhaving a maleic anhydride graft amount of 0.18% by weight and a meltflow rate of 9 g/10 minutes or that having a maleicanhydride-styrene-cograftedpolypropylene/styrene-ethylene.butylene-styrene block copolymer rubberhaving a maleic anhydride graft amount of 0.21% by weight and a meltflow rate of 10 g/10 minutes. These co-modified products are abbreviatedas MS-(PP/SEBS)-1 and MS-(PP/SEBE)-2 hereinafter.

A composition was prepared in the same way as in Example 10 except thatthe cografted product MS-(PP/SEBS)-1 or MS-(PP/SEBE)-2 was used as shownin Table 1, and physical properties thereof were evaluated. Table 2shows the results of the physical property evaluation.

Test pieces prepared from the above composition containing the cograftedproduct MS-(PP/SEBS)-1 or MS-(PP/SEBE)-2 exhibited as excellent Izodimpact strength and penetration impact strength as those of the testpiece of Example 10 prepared from the composition containing theindividually modified products MS-PP-1 and MS-SEBS-1.

EXAMPLE 16

As a graft polypropylene (B), there was used a highly crystallinepropylene block copolymer which was obtained by a slurry polymerizationmethod disclosed in JP-A-60-228504 and which had a melt flow rate of 7.5g/10 minutes, an intrinsic viscosity, measured in tetralin at 135° C.,of 2.18 dl/g, 84% by weight of a polypropylene homopolymer portion (tobe abbreviated as P portion hereinafter) as a first segment formed bypolymerization in a first step and 16% by weight of anethylene-propylene copolymer portion (to be abbreviated as EP portionhereinafter) as a second segment formed by polymerization in a secondstep. The P portion had a molecular structure in which the intrinsicviscosity, measured in tetralin at 135° C., was 1.60 dl/g, the contentof a 20° C. cold xylene-soluble portion was 1.6% by weight, the contentof a boiling heptane-soluble portion was 4.6% by weight and theisotactic pentad of a boiling heptane-insoluble portion was 0,957, andthe EP portion had a molecular structure in which the intrinsicviscosity, measured in tetralin at 135° C., was 5.2 dl/g and theethylene/propylene weight ratio was 37/63 (% by weight). The abovehighly crystalline propylene block copolymer as a starting material isabbreviated as PP-3 hereinafter.

A maleic anhydride-styrene-cograftedpolypropylene/styrene-ethylene.butylene-styrene block copolymer rubberwas prepared in the following manner.

100 Parts by weight of a composition obtained by mixing a polypropylenepowder as a starting material for MS-PP-1 with pellets of astyrene-ethylene.butylene-styrene block copolymer rubber as a startingmaterial for MS-SEBS-1 in a mixing ratio of 25/15, 1.0 part by weight ofmaleic anhydride, 0.5 part by weight of styrene, 0.5 part by weight of aradical initiator prepared by allowing a propylene homopolymer tosupport 8% by weight of 1,3-bis(t-butylperoxyisopropyl)benzene(Sanperox®-TY1-3 supplied by Sanken Kako Co., Ltd.) and 0.1 part byweight of Irganox® 1010 (supplied by Ciba Geigy, Ltd.) as a stabilizerwere uniformly mixed with a Henschel mixer. The resultant mixture wasmelt-kneaded with a twin-screw extruder, model TEX 44 SS-30BW-2Vsupplied by Japan Steel Works Ltd., at a temperature of 220° C. for anaverage residence time of 1.5 minutes to give a maleicanhydride-styrene-cografted polypropylene(A)/styrene-ethylene.butylene-styrene block copolymer rubber having amaleic anhdyride graft amount of 0.25% by weight and a melt flow rate of15 g/10 minutes. This co-modified product is abbreviated asMS-(PP/SEBS)-3. Further, a composition was prepared in the same way asin Examples 1 to 4 by incorporating PBT-1 as a saturated polyester resin(D) and E-MA-GMA-1 as an epoxy group-containing copolymer (E) inproportions as shown in Table 1, and physical properties thereof wereevaluated. Table 2 shows the results of the physical propertyevaluation. When the propylene block copolymer was used as apolypropylene (B), the resultant composition exhibited a greatlyimproved fluidity, and desirable results were obtained with regard toboth fluidity and physical properties.

The thermoplastic resin composition of the present invention producesremarkable effects in that not only the present composition exhibitsexcellent molding properties but also a molded article produced from thepresent composition exhibits excellent physical properties over a moldedarticle produced from individual constituent polymers.

The novel resin composition of the present invention can be processedinto molded articles, a film, a sheet, etc., by a molding method appliedto conventional thermoplastic resins such as injection molding,extrusion molding, etc., and can give molded articles which have wellbalanced properties among stiffness, heat resistance, impact resistance,scratch resistance, coating properties, oil resistance, chemicalresistance, water resistance, etc., and which have excellent appearanceuniformity and smoothness. The thermoplastic resin composition of thepresent invention is suitably useful in fields where especiallyhigh-level heat resistance and impact resistance, low-temperature impactresistance in particular are required.

                                      TABLE 1                                     __________________________________________________________________________           Graft                                                                         polypropylene                                                                            Saturated                                                                           Epoxy group-                                                                            Modified Rubbery                                                                              Poly-                              or graft resin                                                                           polyester                                                                           containing                                                                              rubbery  substance                                                                            propylene                          composition                                                                              resin (F)                                                                           copolymer (G)                                                                           substance (I)                                                                          (H)    (C)                                (wt. %)    (wt. %)                                                                             (wt. %)   (wt. %)  (wt. %)                                                                              (wt. %)                     __________________________________________________________________________    Example 1                                                                            M-PP-1   70                                                                              PBT-1                                                                              5                                                                              E-MA-GMA-1                                                                            10                                                                              M-SEBS-1                                                                             15                                                                              --     --                          Example 2                                                                            M-PP-1   55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                            10                                                                              M-SEBS-1                                                                             15                                                                              --     --                          Example 3                                                                            M-PP-1   40                                                                              PBT-1                                                                             35                                                                              E-MA-GMA-1                                                                            10                                                                              M-SEBS-1                                                                             15                                                                              --     --                          Example 4                                                                            M-PP-1   55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              M-SEBS-1                                                                             20                                                                              --     --                          Example 5                                                                            M-PP-1   55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                            10                                                                              MS-SEBS-1                                                                            15                                                                              --     --                          Example 6                                                                            M-PP-1   55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              MS-SEBS-1                                                                            20                                                                              --     --                          Example 7                                                                            M-PP-1   55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              --       SEBS-1                                                                             20                                                                              --                          Example 8                                                                            M-PP-1   55                                                                              PBT-1                                                                             20                                                                              E-VA-GMA-1                                                                            10                                                                              MS-SEBS-1                                                                            15                                                                              --     --                          Example 9                                                                            MS-PP-1  70                                                                              PBT-1                                                                              5                                                                              E-MA-GMA-1                                                                            10                                                                              M-SEBS-1                                                                             15                                                                              --     --                          Example 10                                                                           MS-PP-1  55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                            10                                                                              MS-SEBS-1                                                                            15                                                                              --     --                          Example 11                                                                           MS-PP-1  55                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              --       SEBS-1                                                                             20                                                                              --                          Example 12                                                                           M-(PP/SEBS)-1                                                                          85                                                                              PBT-1                                                                              5                                                                              E-MA-GMA-1                                                                            10                                                                              --       --     --                          Example 13                                                                           M-(PP/SEBS)-1                                                                          75                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              --       --     --                          Example 14                                                                           MS-(PP/SEBS)-1                                                                         85                                                                              PBT-1                                                                              5                                                                              E-MA-GMA-1                                                                            10                                                                              --       --     --                          Example 15                                                                           MS-(PP/SEBS)-2                                                                         75                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              --       --     --                          Example 16                                                                           MS-(PP/SEBS)-3                                                                         40                                                                              PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                             5                                                                              --       --     PP-3                                                                             35                       Comparative                                                                          --         PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                            10                                                                              --       --     PP-1                                                                             70                       Example 1                                                                     Comparative                                                                          --         PBT-1                                                                             20                                                                              --        --       SEBS-1                                                                             20                                                                              PP-1                                                                             60                       Example 2                                                                     Comparative                                                                          --         PBT-1                                                                             20                                                                              E-MA-GMA-1                                                                            10                                                                              --       SEBS-1                                                                             10                                                                              PP-1                                                                             60                       Example 3                                                                     Comparative                                                                          M-PP-1   60                                                                              PBT-1                                                                             20                                                                              --        --       SEBS-1                                                                             20                                                                              --                          Example 4                                                                     __________________________________________________________________________

                                      TABLE 2                                     __________________________________________________________________________           Physical properties                                                                      Tensile properties                                                            Strength                                                                           Elongation                                                                            Flexural                                                  Melt flow                                                                            at yield                                                                           at      properties                                                rate   point                                                                              fracture point                                                                        Modulus                                                                            Strength                                  No.        (g/10 min)                                                                           (kg/cm.sup.2)                                                                      (%)     (kg/cm.sup.2)                                                                      (kg/cm.sup.2)                             __________________________________________________________________________    Example 1                                                                            0.923                                                                             20.2   193   190    8900 263                                       Example 2                                                                            0.969                                                                             12.3   187   160    9300 261                                       Example 3                                                                            1.021                                                                             2.3    213    90    9400 313                                       Example 4                                                                            0.970                                                                             1.9    170  >200    7800 240                                       Example 5                                                                            0.967                                                                             10.1   195  >200    8300 234                                       Example 6                                                                            0.969                                                                             1.5    169  >200    7700 238                                       Example 7                                                                            0.971                                                                             1.7    172   180    8000 245                                       Example 8                                                                            0.970                                                                             8.6    198   190    8700 246                                       Example 9                                                                            0.925                                                                             16.7   181  >200    7400 223                                       Example 10                                                                           0.971                                                                             7.5    176  >200    7700 221                                       Example 11                                                                           0.968                                                                             1.4    178  >200    8100 224                                       Example 12                                                                           0.924                                                                             18.4   191  >200    8800 261                                       Example 13                                                                           0.970                                                                             1.7    188  >200    7700 215                                       Example 14                                                                           0.922                                                                             16.2   182  >200    7500 256                                       Example 15                                                                           0.969                                                                             1.6    184  >200    7500 211                                       Example 16                                                                           0.973                                                                             4.6    182  >200    7300 208                                       Comparative                                                                          0.970                                                                             1.0    275   100    15100                                                                              410                                       Example 1                                                                     Comparative                                                                          0.968                                                                             1.3    260   150    13500                                                                              371                                       Example 2                                                                     Comparative                                                                          0.971                                                                             1.6    259   170    13100                                                                              368                                       Example 3                                                                     Comparative                                                                          0.967                                                                             2.1    258   160    13400                                                                              368                                       Example 4                                                                     __________________________________________________________________________           Izod impact                                                                            Penetration impact                                                   strength strength (YE/TE) *1                                                                         Thermal                                                                              Rockwell                                        23° C.                                                                     -30° C.                                                                     23° C.                                                                        -30° C.                                                                       deformation                                                                          hardness                                 No.    (kg · cm/cm)                                                                  (J: Joule)    (°C.)                                                                         H.sub.R                                  __________________________________________________________________________    Example 1                                                                            16.0                                                                              5.0  28/48 (D-B)                                                                          19/25 (B)                                                                            104    71                                       Example 2                                                                            17.6                                                                              6.1  27/49 (D-B)                                                                          18/23 (B)                                                                            100    69                                       Example 3                                                                            8.6 5.7  26/47 (D-B)                                                                          12/19 (B)                                                                            101    70                                       Example 4                                                                            43.3                                                                              7.5  28/50 (D)                                                                            22/41 (B)                                                                             91    59                                       Example 5                                                                            26  5.8  27/49 (D-B)                                                                          15/18 (B)                                                                             95    61                                       Example 6                                                                            46.1                                                                              7.7  28/51 (D)                                                                            24/39 (D-B)                                                                           91    58                                       Example 7                                                                            18.4                                                                              6.3  26/48 (D-B)                                                                          20/22 (B)                                                                             94    62                                       Example 8                                                                            17.2                                                                              5.3  25/45 (D-B)                                                                          14/20 (B)                                                                             96    63                                       Example 9                                                                            78  6.1  28/49 (D)                                                                            23/43 (D-B)                                                                           90    68                                       Example 10                                                                           85  8.8  29/52 (D)                                                                            24/44 (D-B)                                                                           95    66                                       Example 11                                                                           68  5.7  27/49 (D-B)                                                                          25/45 (D-B)                                                                           97    68                                       Example 12                                                                           23.5                                                                              6.4  28/50 (D-B)                                                                          19/25 (B)                                                                            103    70                                       Example 13                                                                           85  30.1 29/52 (D)                                                                            24/46 (D-B)                                                                           93    63                                       Example 14                                                                           30.7                                                                              6.6  29/51 (D-B)                                                                          19/27 (B)                                                                            101    69                                       Example 15                                                                           91  38.1 28/52 (D)                                                                            26/45 (D-B)                                                                           90    62                                       Example 16                                                                           95  41.1 29/52 (D)                                                                            27/46 (D-B)                                                                           89    61                                       Comparative                                                                          4.2 2.8  18/21 (B)                                                                            0.3/0.4 (B)                                                                          124    96                                       Example 1                                                                     Comparative                                                                          4.8 3.2  19/25 (B)                                                                            0.5/0.6 (B)                                                                          119    92                                       Example 2                                                                     Comparative                                                                          5.1 3.6  21/25 (B)                                                                            0.7/0.9 (B)                                                                          116    90                                       Example 3                                                                     Comparative                                                                          5.0 3.3  18/20 (B)                                                                            0.6/0.8 (B)                                                                          118    91                                       Example 4                                                                     __________________________________________________________________________     Note)                                                                         *1 Penetration impact strength                                                YE: Yield point energy, TE: Total energy, (D) and (B) indicate a fracture     state, (D) means ductile fracture and (B) means brittle fracture.        

What is claimed is:
 1. A thermoplastic resin composition whichcomprises:(a) 100 parts by weight of a graft resin composition (J)obtained by graft polymerizing at least one unsaturated carboxylic acidor derivative thereof selected from the group consisting of acrylicacid, methacrylic acid, maleic acid, itaconic acid, maleic anhydride anditaconic anhydride onto a mixture of 20 to 98% by weight of acrystalline polypropylene (C) and a rubbery substance (H) which isstyrene-ethylene.butylene-styrene copolymer rubber, the total of (C) and(H) being 100% by weight, the number average molecular weight of thestyrene polymer block in the styrene-ethylene,butylene-styrene copolymerrubber being 1,000 to 200,000, the number average molecular weight ofthe ethylene,butylene copolymer block in thestyrene-ethylene.butylene-styrene copolymer rubber being 1,000 to200,000, and the weight ratio of the styrene polymer block to theethylene.butylene copolymer block being 10:90 to 40:60, (b) 0.1-600parts by weight of at least one saturated polyester resin (F) selectedfrom the group consisting of polyethylene terephthalate and polybutyleneterephthalate, (c) 0.1-300 parts by weight of an epoxy group-containingcopolymer (G) selected from the group consisting of a copolymer ofethylene and an unsaturated epoxy compound and a terpolymer of ethylene,an unsaturated epoxy compound and an ethylenic unsaturated compoundother than ethylene, the unsaturated epoxy compound being at least onemember selected from the group consisting of glycidyl acrylate, glycidylmethacrylate, glycidyl itaconate, allylglycidyl ether, 2-methylglycidylether and styrene-p-glycidyl ether, and the ethylenic unsaturatedcompound other than ethylene being at least one member selected from thegroup consisting of vinyl acetate, methyl acetate, ethyl acetate, methylmethacrylate, vinyl chloride, vinylidene chloride and isobutyl vinylether, the proportion of the unsaturated epoxy compound in the epoxygroup-containing copolymer (G) being 0.1 to 50% by weight, and (d) 0 to1,900 parts by weight per 100 parts by weight of the graft resincomposition (J) of a crystalline polypropylene (C), wherein the amountof graft polypropylene contained in graft resin composition (J) is notless than 5% by weight based on the total amount of the graftpolypropylene and the polypropylene (C) contained in the graft resincomposition (J), the content of the saturated polyester resin (F) in thethermoplastic resin composition being 45 to 1% by weight.
 2. Athermoplastic resin composition according to claim 1, wherein thethermoplastic resin composition further comprises 0.01-300 parts byweight of a filler (L).
 3. A thermoplastic resin composition accordingto claim 2, wherein the unsaturated carboxylic acid or a derivativethereof is maleic anhydride.
 4. A thermoplastic resin compositionaccording to claim 2, wherein the filler (L) is a fiber or an inorganicfiller selected from the group consisting of glass fiber, carbon fiber,talc and mica.
 5. A thermoplastic resin composition according to claim1, wherein the unsaturated carboxylic acid or a derivative thereof ismaleic anhydride.
 6. A thermoplastic resin composition whichcomprises:(a) 100 parts by weight of a graft resin composition (J)obtained by graft polymerizing at least one unsaturated carboxylic acidor derivative thereof selected from the group consisting of acrylicacid, methacrylic acid, maleic acid, itaconic acid, maleic anhydride anditaconic anhydride onto a mixture of a crystalline polypropylene (C) and98-20% by weight of a rubbery substance (H) which isstyrene-ethylene.butylene-styrene copolymer rubber, the total of (C) and(H) being 100 percent by weight, the number average molecular weight ofthe styrene polymer block in the styrene-ethylene, butylene-styrenecopolymer rubber being 1,000 to 200,000, the number average molecularweight of the ethylene.butylene copolymer block in thestyrene-ethylene.butylene-styrene copolymer rubber being 1,000 to200,000, and the weight ratio of the styrene polymer block to theethylene.butylene copolymer block being 10:90 to 40:60, (b) 0.1-600parts by weight of at least one saturated polyester resin (F) selectedfrom the group consisting of polyethylene terephthalate and polybutyleneterephthalate, (c) 0.1-300 parts by weight of an epoxy group-containingcopolymer (G) selected from the group consisting of a copolymer ofethylene and an unsaturated epoxy compound and a terpolymer of ethylene,an unsaturated epoxy compound and an ethylenic unsaturated compoundother than ethylene, the unsaturated epoxy compound being at least onemember selected from the group consisting of glycidyl acrylate, glycidylmethacrylate, glycidyl itaconate, allylglycidyl ether, 2-methylglycidylether and styrene-p-glycidyl ether, and the ethylenic unsaturatedcompound other than ethylene being at least one member selected from thegroup consisting of vinyl acetate, methyl acetate, ethyl acetate, methylmethacrylate, vinyl chloride, vinylidene chloride and isobutyl vinylether, the proportion of the unsaturated epoxy compound in the epoxygroup-containing copolymer (G) being 0.1 to 50% by weight, and (d) 0 to1,900 parts by weight per 100 parts by weight of the graft resincomposition (J) of a crystalline polypropylene (C), wherein the amountof graft polypropylene contained in graft resin composition (J) is notless than 5% by weight based on the total amount of the graftpolypropylene and the polypropylene (C) contained in the graft resincomposition (J), the content of the saturated polyester resin (F) in thethermoplastic resin composition being 45 to 1% by weight.
 7. Athermoplastic resin composition according to claim 6, wherein thethermoplastic resin composition further comprises 0.01-300 parts byweight of a filler (L).
 8. A thermoplastic resin composition accordingto claim 7, wherein the unsaturated carboxylic acid or a derivativethereof is maleic anhydride.
 9. A thermoplastic resin compositionaccording to claim 7, wherein the filler (L) is a fiber or an inorganicfiller selected from the group consisting of glass fiber, carbon fiber,talc and mica.
 10. A thermoplastic resin composition according to claim6, wherein the unsaturated carboxylic acid or a derivative thereof ismaleic anhydride.